阻燃TPU
FR87A BLACK
Revised 20150301
TYPE : FR87A BLACK TPU is 87A aromatic Polyether-Based , Halogen based Thermoplastic Polyurethane
Compound
Feature : Matte surface compound , Good mechanical properties
Application : Wire & Cable extrusion , Injection molding
MECHANICAL PROPERTIES |
TEST METHOD |
UNIT
|
VALUE* |
Hardness | ISO 868 | shore A/D | 87A+/-3 |
Density | ISO 2781 | g/cm3 | 1.28 |
Tensile strength | ISO 527 | MPa | 25 |
Elongation | ISO 527 | % | 580 |
Tensile Stress at | |||
50 % Elongation | MPa | 6.4 | |
100 % Elongation | MPa | 7.5 | |
300 % Elongation | MPa | 12.6 | |
Tear Strength( Die C ) | |||
nicked | ISO 34-1B | KN/m | 74 |
unnicked | 128 | ||
Oxygen Index | % | 28 | |
Vertical burn test | UL94 | -- | V0 |
PROCESS CONDITIONS
Before process, the material must be dried at a dehumidfying drier, or at least a hot air drier. The drying condition should be: temperature 104°C 3 hours or above (should less than 8 hours), the moisture level must be below 0.03%before process.
Furthermore, an extruder with an L/D ratio of 25+ is recommended.
Melt temperature and die temperature is very important to obtain good surface quality. Too high temperature will cause gloss surface, too cool will cause rough surface.
Also, line speed will affect the surface quality as well, lower line speed is tend to gloss surface, while higher speed will cause matte surface.
Zone | Temperature |
Temp. 1 | 170°C |
Temp. 2 | 180°C |
Temp. 3 | 190°C |
Temp. 4 | 195°C |
Adaptor | 195°C |
Die | 190°C |
SUPPLY FORM AND STANDARD PACKAGING 25kgs each bag.
* This typical value, not product specification